Two Part Water Based Epoxy Resin Floor Emulsion Coating Paint

Min Order

1
Product Unit

Pieces
Origin

China Mainland
Payment
Contact Now Start Order

Description

Product Detail

Two Part Water Based Epoxy Resin floor Emulsion Coating Paint WQ-EP503

EP503 epoxy resin features:

? Nonionic self-emulsifying epoxy

? Small particle size of emulsion

? Good film-forming properties

? Low VOC

EG043 curing agent features:

? Phenol modified aliphatic amine

? Good hydrophobic property

? Good compatibility

? Good resistance to media

EP503+EG043 features:

Film thickness: 50-60um at 80? for 30 mins, salt fog resistance: over 800 hours

Technical index of product:

Composition:epoxy resin,cosolvent,water

Appearance:milky white uniform liquid

Non-volatile matters(%):50±2

Viscosity(m Pa.s):=2000

PH value:4.0~8.0

Epoxy value(to solid):0.18~0.22

Product characteristics:

(1) The product contains no heavy metal and meets Rohs requirements;

(2) Excellent anti-rust and anti-corrosivity;

(3) Excellent water resistance and salt fog resistance;

(4) Good applicability

Applications:

As a water based epoxy emulsion, this product can prepare water based epoxy flooring coating, the paint for railway, locomotive, bridge and container, water based epoxy anti-corrosive paint, household paint and metal paint.

Storage:

This product should be stored in sealed containers at a cool place at 5-40?, with the shelf life of 6 months. The expired products can be used after passing the test.

WQ-EP503 Test Form

Primer Test Result

Item		Test Result	Test Method
Physical and Chemical Properties	Original paint	Uniform liquid	Visual check
	Paint film color	Light grey	Visual check
	Hiding power, g/m2	80	GB/T 1720-1979
	Original paint viscosity (T-4 cup at 25o) S	132s	GB/T 1723-1993
	Fineness, micron	=30	GB/T1724-1979
	Non-volatile matters, %	52	GB/T1725-2007
	Surface drying time, min at 23?	20	GB 1728-1979
	Hard drying time, h at 25?	5	GB 1728-1979
	Baking time, min at 65?	30	GB/T1728-1979
	Pot life, h at 25?	3	HG/T3668-2000-5.9
Mechanical Properties	Hardness (pencil)	H	GB/T 6739-2006
	Flexibility, mm	1	GB/T 1731-1993
	Impact resistance, KgNaN/50cm	pass	GB/T 1732-1993
	Grinability (20 times,320# sand paper	grindable	GB/T1770-2008
	Adhesion (Cross-cut tape test)	1	GB/T9286-1998
	Adhesion (circle-cut tape test)	1	GB/ 1720-1979
	Matching	Compatibility with other coating	Good
Corrosion resistance	Water resistance at 23?	240 h , no bubbling, peeling off and rusting	GB/T 1733-1993
	Alkaline resistance (at 25?, 0.1N NaOH)	48 h	GB/T9274-1998
	Acid resistance (at 25?, 0.1N H2SO4)	48 h, no bubbling	GB/T9274-1998
	Oil resistance (at 25?,10# Transformer oil)	48 h, no change	HGT/ 9274-1998
	Temperature alternating resistance (at -40? +60?)
	Salt fog resistance (480h)	Bubbling at cross, not bigger than 2 mm at a single side	GB 1771-2007

????.jpg

Other Product:

product name	non- volatile	epoxy equivalent	PH	viscosity (mPa.s)	specific gravity	properties	application
WQ-LP603	50±2	1000±50	6-8	200-900	1.10±0.01	small particle size uniform coating,good mechnical stability,can grind	two-component epoxy antirust paint
WQ-LP604	50±2	1000±50	6-8	200-900	1.10±0.01	good adhesion and salt fog-spray resistance	two-component epoxy antirust paint
WQ-LG040	40±2	350±30	8-10	3000-7000	1.06±0.01	quick crosslinking speed, excellent salt fog-spray resistance	used with epoxy emulsion,two-component epoxy antirust paint
WQ-LG043	43±2	350±30	8-10	3000-7000	1.06±0.01	long construction time limit,good salt fog-spray resistance	used with epoxy emulsion,two-component epoxy antirust paint